Characterisation of the SEI formed on natural graphite in PC-based electrolytes
Uppsala universitet, Teknisk-naturvetenskapliga vetenskapsområdet, Kemiska sektionen, Institutionen för materialkemi. Fysiska sektionen, Institutionen för fysik och materialvetenskap, Fysik I. Uppsala universitet, Teknisk-naturvetenskapliga vetenskapsområdet, Kemiska sektionen, Institutionen för materialkemi, Strukturkemi. strukturkemi.
Uppsala universitet, Teknisk-naturvetenskapliga vetenskapsområdet, Kemiska sektionen, Institutionen för materialkemi. Fysiska sektionen, Institutionen för fysik och materialvetenskap, Fysik I. Uppsala universitet, Teknisk-naturvetenskapliga vetenskapsområdet, Kemiska sektionen, Institutionen för materialkemi, Strukturkemi. strukturkemi.
Fysiska institutionen. Fysiska sektionen, Institutionen för fysik och materialvetenskap, Fysik I. Uppsala universitet, Teknisk-naturvetenskapliga vetenskapsområdet, Kemiska sektionen, Institutionen för materialkemi, Strukturkemi. (Fysik 1)
Fysiska institutionen. Fysiska sektionen, Institutionen för fysik och materialvetenskap, Fysik I. Uppsala universitet, Teknisk-naturvetenskapliga vetenskapsområdet, Kemiska sektionen, Institutionen för materialkemi, Strukturkemi. (Fysik 1)
Vise andre og tillknytning
2004 (engelsk)Inngår i: Electrochimica Acta, nr 49, s. 4939-4947Artikkel i tidsskrift (Fagfellevurdert) Published
Abstract [en]

The origin of the different Li+ intercalation behavior of raw and jet-milled natural graphite has been investigated. Jet-milled graphite is found to cycle reversibly in equal solvent mixture of propylene carbonate (PC) and etylene carbonate (EC), whereas raw graphite does not. Using both Al Ka and synchrotron radiation (SR) Photoelectron Spectroscopy, new insight is obtained inti the formation of the solid electrolyte interphase (SEI) on the two different graphite materials during electrochemical cycling in 1 M LiPF6 in either PC:EC (1:1) or in PC with 5% vinylene carbonate (VC) as additive. Solvent reduction products are found at the surface of both raw and jat-milled graphite cycled in PC:EC (1:1), but differed in composition. The addition of VC reduces primarily the quantities of salt reaction products (LiF and LixPFy compounds) and produces a mainly organic SEI layer. Electron diffraction from the edges for raw and jet-milled graphite particles shows a physical barrier hindering PC co-intercalation and faciltating the formation of a stable SEI layer.

sted, utgiver, år, opplag, sider
2004. nr 49, s. 4939-4947
Emneord [en]
natural graphite, photoelectron spectroscopy, propylene carbonate, vinylene carbonate, solid electrolyte interphase
HSV kategori
Identifikatorer
URN: urn:nbn:se:uu:diva-66872OAI: oai:DiVA.org:uu-66872DiVA, id: diva2:94783
Tilgjengelig fra: 2007-02-13 Laget: 2007-02-13 Sist oppdatert: 2011-01-12

Open Access i DiVA

Fulltekst mangler i DiVA

Personposter BETA

Rensmo, HåkanSiegbahn, HansEdström, Kristina

Søk i DiVA

Av forfatter/redaktør
Rensmo, HåkanSiegbahn, HansEdström, Kristina
Av organisasjonen

Søk utenfor DiVA

GoogleGoogle Scholar

urn-nbn

Altmetric

urn-nbn
Totalt: 877 treff
RefereraExporteraLink to record
Permanent link

Direct link
Referera
Referensformat
  • apa
  • ieee
  • modern-language-association
  • vancouver
  • Annet format
Fler format
Språk
  • de-DE
  • en-GB
  • en-US
  • fi-FI
  • nn-NO
  • nn-NB
  • sv-SE
  • Annet språk
Fler språk
Utmatningsformat
  • html
  • text
  • asciidoc
  • rtf