Synthesis and characterisation of solid low-Tg polymer electrolytes for lithium-ion batteries
Uppsala University, Disciplinary Domain of Science and Technology, Chemistry, Department of Chemistry - Ångström.
2014 (English)Independent thesis Advanced level (professional degree), 300 HE creditsStudent thesis
Abstract [en]

Electrolytes of poly(trimethylene carbonate-co-ε-caprolactone), poly(TMC-co-CL), and LiTFSI have been prepared and characterised. The copolymers were analysed with GPC and NMR, which showed that random high molecular weight copolymers of desired compositions had been obtained. The electrolytes with varied salt concentration were examined with TGA, DSC, FTIR and impedance spectroscopy. The highest ionic conductivities were measured for the copolymer of 60:40 ratio of TMC:CL and for the homopolymer poly(ε-caprolactone), PCL, both electrolytes with 28 wt% LiTFSI. The ionic conductivity was measured to of the order of 10−3 S cm−1 for the PCL electrolyte and 10−4 S cm−1 for the 60:40 copolymer at 50 °C. 

Place, publisher, year, edition, pages
2014. , 28 p.
UPTEC K, ISSN 1650-8297 ; 14013
Keyword [en]
National Category
Chemical Engineering
URN: urn:nbn:se:uu:diva-226754OAI: oai:DiVA.org:uu-226754DiVA: diva2:727186
Educational program
Master Programme in Chemical Engineering
Available from: 2014-08-06 Created: 2014-06-19 Last updated: 2014-08-06Bibliographically approved

Open Access in DiVA

Report(1183 kB)200 downloads
File information
File name FULLTEXT01.pdfFile size 1183 kBChecksum SHA-512
Type fulltextMimetype application/pdf

By organisation
Department of Chemistry - Ångström
Chemical Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 200 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 354 hits
ReferencesLink to record
Permanent link

Direct link