Compressive, diametral tensile and biaxial flexural strength of cutting-edge calcium phosphate cements
2016 (English)In: Journal of The Mechanical Behavior of Biomedical Materials, ISSN 1751-6161, E-ISSN 1878-0180, Vol. 60, 617-627 p.Article in journal (Refereed) Published
Calcium phosphate cements (CPCs) are widely used in bone repair. Currently there are two main types of CPCs, brushite and apatite. The aim of this project was to evaluate the mechanical properties of particularly promising experimental brushite and apatite formulations in comparison to commercially available brushite- and apatite-based cements (chronOS™ Inject and Norian® SRS®, respectively), and in particular evaluate the diametral tensile strength and biaxial flexural strength of these cements in both wet and dry conditions for the first time. The cements׳ porosity and their compressive, diametral tensile and biaxial flexural strength were tested in wet (or moist) and dry conditions. The surface morphology was characterized by scanning electron microscopy. Phase composition was assessed with X-ray diffraction. It was found that the novel experimental cements showed better mechanical properties than the commercially available cements, in all loading scenarios. The highest compressive strength (57.2±6.5 MPa before drying and 69.5±6.0 MPa after drying) was found for the experimental brushite cement. This cement also showed the highest wet diametral tensile strength (10.0±0.8 MPa) and wet biaxial flexural strength (30.7±1.8 MPa). It was also the cement that presented the lowest porosity (approx. 12%). The influence of water content was found to depend on cement type, with some cements showing higher mechanical properties after drying and some no difference after drying.
Place, publisher, year, edition, pages
2016. Vol. 60, 617-627 p.
Calcium phosphate cement; Brushite; Apatite; Compressive strength; Tensile strength; Flexural strength
IdentifiersURN: urn:nbn:se:uu:diva-284218DOI: 10.1016/j.jmbbm.2016.03.028ISI: 000378969100055PubMedID: 27082025OAI: oai:DiVA.org:uu-284218DiVA: diva2:920060
FunderThe Swedish Foundation for International Cooperation in Research and Higher Education (STINT), IG2011-2047Swedish Research Council, 621-2011-6258