Adhesion of CVD coatings on new cemeted carbides
Uppsala University, Disciplinary Domain of Science and Technology, Technology, Department of Engineering Sciences, Applied Materials Sciences.
2016 (English)Independent thesis Advanced level (professional degree), 20 credits / 30 HE creditsStudent thesisAlternative title
Vidhäftning mellan keramiskt skikt och hårdmetall med alternativ bindefas (Swedish)
Abstract [en]

Steel turning inserts cemented carbides have a binder phase consisting of cobalt (Co). However, in recent years a study from the United States National Toxicity Program (NTP) found that cobalt powder is carcinogenic upon inhalation. The European Union's REACH have therefore also classified cobalt powder as carcinogenic upon inhalation. The worldwide search to find a replacement has therefore lately intensified. It is important that the alternative binder phase has no negative effects on the properties of the insert. In this thesis the adhesion between a multilayer ceramic chemical vapor deposition (CVD) coating and a cemented carbide with the alternative binder phases consisting of iron (Fe), nickel (Ni) and cobalt (Co) has been studied.

First of all, the fracture surfaces showed that the CVD coating was able to grow on all cemented carbides, regardless of which binder phase. To evaluate the adhesion, scratch tests were performed on all samples. The results from the scratch tests were not as expected. No chipping of the coating down to the cemented carbide occurred on any of the samples and the samples with the hardest cemented carbide did not get the highest critical load, which it should according to the literature if all other parameters were the same. Instead the sample with the binder phase consisting of 73 wt% iron and 27 wt% nickel had the highest critical load. This is thought to be due to that during the scratch test the binder phase in this cemented carbide would most likely transform into deformation martensite.

Place, publisher, year, edition, pages
2016. , 41 p.
UPTEC Q, ISSN 1401-5773 ; 16015
Keyword [en]
cemented carbide, adhesion, alternative binder phase, CVD coating, hard metal
National Category
Metallurgy and Metallic Materials Manufacturing, Surface and Joining Technology Other Materials Engineering Composite Science and Engineering
URN: urn:nbn:se:uu:diva-298648OAI: oai:DiVA.org:uu-298648DiVA: diva2:946733
External cooperation
Sandvik Coromant
Educational program
Master Programme in Materials Engineering
Available from: 2016-07-06 Created: 2016-07-05 Last updated: 2016-07-06Bibliographically approved

Open Access in DiVA

fulltext(1774 kB)44 downloads
File information
File name FULLTEXT01.pdfFile size 1774 kBChecksum SHA-512
Type fulltextMimetype application/pdf

By organisation
Applied Materials Sciences
Metallurgy and Metallic MaterialsManufacturing, Surface and Joining TechnologyOther Materials EngineeringComposite Science and Engineering

Search outside of DiVA

GoogleGoogle Scholar
Total: 44 downloads
The number of downloads is the sum of all downloads of full texts. It may include eg previous versions that are now no longer available

Total: 150 hits
ReferencesLink to record
Permanent link

Direct link